Gadolinium gallium garnet

Product Type: Gadolinium gallium garnet (Gd3Ga5O12) crystal substrate Product Description: Gadolinium gallium garnet (GGG) is used for a magneto-optical film (YIG thin film or BIG) a special substrate in the optical communication apparatus, YIG or BIG films are 1.3 and 1.5 of the optical isolator core components of different crystal … Read More

Yttria-stabilized Zirconium Oxide for VIS and IR-range

Formula ZrO2:Y (9.5 mol% Y2O3) Growth method Skull melting Max. sizes, (mm) Ø50.8 Transmission range, (µm) (Thickness 15 mm) 0.43…

Zinc Selenide for VIS and IR-range

Formula ZnSe Growth method Chemical vapour deposition Max. sizes, (mm) Ø100 Transmission range, (µm) (Thickness 10 mm) 0.55 – 18.0…

Zinc Sulfide for IR-range

Formula ZnS Growth method Chemical vapor deposition Max. sizes, (mm) Ø150 Transmission range, (µm) (Thickness 10 mm) 1.0 – 13.0…

ZnS for VIS and IR-range

Formula ZnS Growth method Chemical Vapor Deposition Max. sizes, (mm) Ø180 Transmission range, (µm) (Thickness 10 mm) 0.4 – 12.5…

Yttrium Orthovanadate for VIS and IR-range

Formula YVO4 Growth method Czochralski method Max. sizes, (mm) Ø25 Transmission range, (µm) (Thickness 1 mm) 0.4 – 5.0 Structure…

Yttrium-Aluminum-Garnet (YAG) for VIS and IR-range

Formula Y3Al5O12 Growth method Czochalski technique Max. sizes, (mm) 80 Transmission range, (µm) (Thickness 10 mm) 0.3 – 5.0 Structure…

Titanium Oxide (Rutile) for VIS and IR-range

Formula TiO2 Growth method Verneuil technique Max. sizes, (mm) Ø 25.4 Transmission range, (µm) (Thickness 6 mm) 0.43 – 6.0…

Silicon for IR-range

Formula Si Growth method Czochalski technique Max. sizes, (mm) Ø150 Transmission range, (µm) (Thickness 2 mm) 1.2 – 15.0 Structure…

Magnesium Oxide for VIS and IR-range

Formula MgO Growth method Flux melt Max. sizes, (mm) Ø50.8 Transmission range, (µm) (Thickness 1 mm) 0.3 – 7.0 Structure…

Magnesium Fluoride for UV, VIS and IR-range

Formula MgF2 Growth method Stockbarger technique Max. sizes, (mm) Ø90 Transmission range, (µm) (Thickness 10 mm) 0.13 – 7.0 Structure…

Lithium Niobate for VIS and IR-range

Formula LiNbO3 Growth method Czochralski method Max. sizes, (mm) Ø76.2 Transmission range, (µm) (Thickness 1 mm) 0.4 – 5.0 Structure…

Lithium Fluoride for UV, VIS and IR-range

Formula LiF Growth method Stockbarger technique Max. sizes, (mm) Ø150 Transmission range, (µm) (Thickness 10 mm) 0.12 – 6.5 Structure…

Germanium for IR-range

Formula Ge Growth method Czochralski technique Max. sizes, (mm) Ø200 Transmission range, (µm) (Thickness 10 mm) 2.0 – 18.0 Structure…

Calcium Fluoride for UV, VIS and IR-range

Formula CaF2 Growth method Stockbarger technique Max. sizes, (mm) Ø200 Transmission range, (µm) (Thickness 10 mm) 0.15 – 9.0 Structure…

Barium Fluoride for UV, VIS and IR-range

Formula BaF2 Growth method Stockbarger technique Max. sizes, (mm) Ø150 Transmission range, (µm) (Thickness 10 mm) 0.18 – 12.0 Structure…

Aluminium oxide – Sapphire for VIS and IR-range

Formula Al2O3 Growth method Czochralski technique Brigdeman technique Max. sizes, (mm) Ø150 Transmission range, (_m) (Thickness 10 mm) 0.17 –…